Shanghai Daoqin Plastics Co., Ltd.

DuPont ™ Fusabond® N493 is types acid modified ethylene copolymer.

DuPont 凡事邦 resin is function 化（ generally through maleic anhydride grafted ） modified polymer, used for bonding use in toughened, filling and mixed combined composite/compounding material in different type type polymer. 凡事邦 product series modified ethylene acrylic ester oxidation carbon terpolymer, ethylene -乙 acid ethylene ester （EVA） polymer, polyethylene (PE), metallocene polyethylene (PE), 乙丙橡胶 and polypropylene (PP).

凡事邦 main applications industrial product, high filling injection molding and extrusion composite/compounding material, related grade can improvement nylon tough property, as is bonding use or used for improvement polyethylene (PE) recycling material versus property, is rear packaging recycling plan increase in property can and value

　　 density:0.88g/cm3

　　 melt flow index (190°C/2.16kg):3.7 g/10 min

　　 flexural modulus （.05in/min, 23°C）: 3258 psi(22 MPa)

　　 tensile elongation @ fracture （V type,50mm/min, 23°C）:587 %

　　 tensile elongation @ fracture （V type, 550mm/min, 23°C）:551 %

　　 tensile strength @ fracture （V type, 50mm/min, 20°C）:2085 psi(14 MPa)

　　 tensile strength @ fracture （V type, 50mm/min, 23°C）:933 psi(6 MPa)

　　 hardness hardness （D）:30

　　 melting point （Dsc）: 58℃(136.4℉)

　　凝 solid (DsC): 42°C (107.6°F)

　　玻璃转换 temperature degree: 49℃(-56.2℉) (DSC)

　　维卡 soft 化点:42°C (107.6F)

　　 maleic anhydride grafted rate high polyamide (PA) blending material modifier;

　　 polyolefin electrical cable combined material high modifier;

　　 high 尔夫球罩 mixed combined material;

　　 polyolefin and metal, polyamide (PA), fiber and glass fiber between increase agent or viscous promote agent.

　　1, as is polyolefin 烟(PP/PE)一木 powder composite/compounding material (WPC) compatibilizer and coupling agent, can in between surface generate strong/high 介面结 combined, meanwhile can reduce powder water property, improve/increase powder and plastics between versus property and dispersion property; make composite/compounding material force property can obvious improve/increase.

　　2, as is coupling agent, can in flame retardant mixed material in machine material (如矿 material, hydrogen oxidation 镁, hydrogen oxidation aluminum, carbon acid and other) and polymer (PP, PE, EVA) between 建立起 strong/high combined force, improves electrical cable flexibility property, flame retardant property and force strong/high degree.

　　3, can used as thermoplastic property resin impact modifier 如PA, PP and other (N series).

　　25公斤/包

　　 packaging maintain 密封并存放 in anionic drying 且通风良 good 方, 避免直接 day 晒.