Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625 - Products

Product Details

Basic Parameters

ENGINEERING PLASTICS

Kaneka mbs B564 high impact resistance 击 property 不 transparent PVC modified toughening agent Kaneka impact resistant agent B625

default

🎯 典 type application areas

impact resistanttoughened

polyvinyl chloride (PVC) processing property 改 good 用 impact resistant modifier B-564<

📖 product introduction

Model ：KANE ACE B-564(B564) Brand ： Japan Kaneka kaneka has 效物质 content ：99.5（％） product specifications ：20KG/包产品颜色：白色 powder 末 CAS：SGS主要 applications ： impact resistant 、增强、 toughened polyvinyl chloride (PVC) processing property 改 good 用 impact resistant modifier B-564Kane ACE B-564 is Kaneka 化学新开发专门 used for polyvinyl chloride (PVC) 注射 molding impact resistant modified 用 resin （MBS resin ）。Kane ACE B-564对于较高温，低剪切领域 processing 注射 molding has good 好分散 property 。特别对延 property 破坏领域 impact 强 degree...

⚙️ processing 参数参考

processing temperature 范围

200-260°C

mold temperature

40-80°C

drying conditions

80°C / 3h

干燥 time

0.03%

📋 详细 technology 信息

📋 认证 and 合规信息

🧪 化学耐受 performance

优异 ✅稀酸/稀碱盐溶液醇类脂肪烃

good 好 ✔矿物油(短期)洗涤 agent

受限 ⚠芳香烃halogen 代烃酮类ester 类

避免 ❌丙酮苯甲苯DMF

🌟 material material 优势

AS/SAN（丙烯腈-苯乙烯 copolymer ）比PS具 has 更高刚 property 、 chemical resistance and heat resistant property ，同时保持 good 好 transparent degree 。AS广泛 used for 化妆品容器、厨房用品、仪表壳体等要求 transparent and 刚 property 场合。

📦 储存 and 处理建议

AS/SAN pellets 储存条件同PS。 processing 前80°C干燥2小时。 transparent material 注意防尘防污染。

🌍

RoHS 合规

符合欧盟RoHS指令

🏭

ISO 认证

质量管理体系

✅

quality assured

原厂正品

更多 engineering plastics Model 请访问daoqinsh.com

📐 详细物 property 参数表

测试项目	典 type 值	测试标准	单位
density	1.06-1.10	ASTM D792	g/cm³
melt flow index (MFR)	1-30	ASTM D1238	g/10min
玻璃化转变 temperature (Tg)	105-115	ASTM D3418	°C
透光率	85-90	ASTM D1003	%
tensile strength	55-70	ASTM D638	MPa
断裂伸长率	2-4	ASTM D638	%
flexural modulus	3000-3500	ASTM D790	MPa
flexural strength	90-110	ASTM D790	MPa
悬臂梁缺口 impact	20-30	ASTM D256	J/m
heat deflection temperature (HDT) (0.45MPa)	95-105	ASTM D648	°C
体积电阻率	>10¹⁴	ASTM D257	Ω·cm
water absorption (24h)	0.2-0.3	ASTM D570	%
molding shrinkage	0.2-0.6	ASTM D955	%
UL94 flame retardant rating	HB	UL 94	—

* 以上数据 is 典 type 参考值，具体以原厂TDS is 准

If you have any questions about Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625, or would like to request Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625 datasheet, MSDS, ROHS test report, SGS report, REACH certificate, FDA certificate, EU regulation certificate, UL certificate, or COC/COA report, please call our service hotline +86-192-7986-4570, or click Contact Us to leave us a message.

Product Features

Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625 Properties, Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625 Product Parameters, Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625 Performance Data, Kaneka mbs B564 high impact resistance property not transparent PVC modified toughening agent Kaneka impact resistant agent B625 Factory Report, MSDS, Material Safety Data Sheet, UL Yellow Card, SGS Report, RoHS, Food Grade Certification, NSF Drinking Water Standard, Product Information, Product Performance, Factory Report, Original Packaging, Authorized Distributor, Heat Deflection Temperature, Melt Index, Flow Coefficient, Impact Resistance, Impact Strength, Low Temperature Toughness, Low Temperature Impact Resistance, Melt Flow Rate, Processing Technology, Processing Parameters, Processing Temperature, EU RoHS, German FDA, US FDA, Japan FDA