Product Details

Basic Parameters

Chang Chun 11G6-201

CCP · PA6 · flame retardant reinforced grade (PA6/30% glass fiber (GF) /V0)

density (g/cm³)

1.4

MFR/关键参数

—

product features

30% glass fiber reinforced flame retardant PA6，UL94 V-0， high strength flame retardant

application areas

electronic connectors 、电气开关、 flame retardant 结构件

product introduction

Chang Chun 化工(CCP) is 亚洲领先 engineering plastics manufacturing 商，旗下LONGLITE Brand covering PBT、PA6、PA66 and TPEE等产品 line ，以 excellent performance and 稳定品质著称， widely used in 电子电气、汽车、工业 and 消费品等领域。

⚙️ injection molding processing 参数参考

melt temperature 范围

240-270°C

mold temperature

60-90°C

drying conditions

80°C / 4h

injection pressure

80-130 MPa

molding shrinkage

0.7-1.5%

processing 备注

强 moisture absorption property ，除湿干燥机必须

🧪 化学耐受 performance

优异 ✅矿物油/ lubricated 脂燃 material 油液压油醇类醚类

good 好 ✔弱碱洗涤 agent芳香烃(短期)

受限 ⚠强酸酚类甲酸浓碱

避免 ❌浓硫酸浓盐酸甲酸(溶解)间甲酚

🌟 material material 优势

PA6（ nylon 6 /聚己内酰胺）具 has excellent mechanical properties 、 wear resistance and 自 lubricated property 。PA6广泛 used for automotive parts 、 electronic connectors 、机械零件、纺织 fiber 等领域。 glass fiber reinforced 后 performance 大幅提升，可替代金属结构件。

📋 认证 and 合规信息

🌍

RoHS 合规

符合欧盟RoHS指令

🏭

ISO 认证

质量管理体系认证

✅

REACH

欧盟化学品合规

💧

quality assured

原厂正品保障

📦 储存 and 处理建议

PA6 resin 具 has 强 moisture absorption property (平衡含水率3.0%)，必须储存 in 干燥、密封环境 in 。 processing 前80°C干燥4小时(除湿干燥机必须)，含水率控制 in 0.1%以下。开封后应尽快使用，未用完需重新密封并放置干燥 agent 。

产地

Taiwan / China 大陆

material 筒 temperature

230-280°C

mold temperature

40-100°C

干燥要求

120°C / 4小时

daoqinsh.com · Daoqin plastics · Chang Chun CCP 专业供应商

📐 详细物 property 参数表

测试项目	典 type 值	测试标准	单位
density	1.12-1.15	ASTM D792	g/cm³
melt flow index (MFR)	5-80	ASTM D1238	g/10min
melt temperature	215-225	ASTM D3418	°C
tensile strength (干态)	60-85	ASTM D638	MPa
tensile strength (调湿态)	45-60	ASTM D638	MPa
断裂伸长率(干态)	50-300	ASTM D638	%
flexural modulus (干态)	2500-3000	ASTM D790	MPa
flexural strength (干态)	85-120	ASTM D790	MPa
悬臂梁缺口 impact (干态)	50-150	ASTM D256	J/m
洛氏 hardness	R118-R122	ASTM D785	—
heat deflection temperature (HDT) (0.45MPa)	180-210	ASTM D648	°C
heat deflection temperature (HDT) (1.8MPa)	65-80	ASTM D648	°C
line property thermal expansion coefficient	60-80	ASTM D696	10⁻⁶/°C
体积电阻率	>10¹²	ASTM D257	Ω·cm
介电强 degree	15-25	ASTM D149	kV/mm
friction 系数	0.15-0.35	ASTM D1894	—
water absorption (24h/饱 and)	1.8/3.0	ASTM D570	%
molding shrinkage	0.7-1.5	ASTM D955	%
UL94 flame retardant rating	V-2	UL 94	—

* 以上数据 is 典 type 参考值，具体以原厂TDS is 准

If you have any questions about Chang Chun (Taiwan) 11G6-201 PA6 flame retardant reinforced grade (/30% glass fiber (GF) /V0, or would like to request Chang Chun (Taiwan) 11G6-201 PA6 flame retardant reinforced grade (/30% glass fiber (GF) /V0 datasheet, MSDS, ROHS test report, SGS report, REACH certificate, FDA certificate, EU regulation certificate, UL certificate, or COC/COA report, please call our service hotline +86-192-7986-4570, or click Contact Us to leave us a message.

Product Features

Chang Chun (Taiwan) 11G6-201 PA6 flame retardant reinforced grade (/30% glass fiber (GF) /V0 Properties, Chang Chun (Taiwan) 11G6-201 PA6 flame retardant reinforced grade (/30% glass fiber (GF) /V0 Product Parameters, Chang Chun (Taiwan) 11G6-201 PA6 flame retardant reinforced grade (/30% glass fiber (GF) /V0 Performance Data, Chang Chun (Taiwan) 11G6-201 PA6 flame retardant reinforced grade (/30% glass fiber (GF) /V0 Factory Report, MSDS, Material Safety Data Sheet, UL Yellow Card, SGS Report, RoHS, Food Grade Certification, NSF Drinking Water Standard, Product Information, Product Performance, Factory Report, Original Packaging, Authorized Distributor, Heat Deflection Temperature, Melt Index, Flow Coefficient, Impact Resistance, Impact Strength, Low Temperature Toughness, Low Temperature Impact Resistance, Melt Flow Rate, Processing Technology, Processing Parameters, Processing Temperature, EU RoHS, German FDA, US FDA, Japan FDA