Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer - Products

Product Details

Basic Parameters

Clariant

Clariant AddWorks TFB 117 polyamide (PA) nylon 用光热协同 stabilizer

default

📖 product introduction

Clariant AddWorks® TFB 117 stabilizer ： is polyamide (PA) fiber 赋予可持续强 degree and flexibility degree Clariant CLARIANT AddWorks TFB 117 is 一款专 is polyamide (PA) nylon 设计多功能光热协同 stabilizer ，具 has 卓越兼容 property and 可持续 property 优势，可提高 polyamide (PA) 可纺 property 、 heat stabilized property and 光稳定 property ，同时提高耐洗涤 property 。它 suitable for PA6、PA66、PA11、PA12等多种 polyamide (PA) resin 聚合过程， widely used in 服装、地毯 and 工业 polyamide (PA) fiber 。通过 improves polyamide (PA) heat stabilized property 、可纺 property and 染色 property...

⚙️ processing 参数参考

processing temperature 范围

200-260°C

mold temperature

40-80°C

drying conditions

80°C / 3h

干燥 time

0.03%

📋 详细 technology 信息

Clariant AddWorks® TFB 117 stabilizer ： is polyamide (PA) fiber 赋予可持续强 degree and flexibility degree

📋 认证 and 合规信息

🧪 化学耐受 performance

优异 ✅矿物油/ lubricated 脂燃 material 油液压油醇类

good 好 ✔弱碱洗涤 agent醚类

受限 ⚠强酸酚类甲酸浓碱

避免 ❌浓硫酸浓盐酸甲酸(溶解)

🌟 material material 优势

nylon (PA) is 应用最广泛 engineering plastics 家族，具 has high strength 、 high toughness 、 wear resistant 自 lubricated 、耐油等优异 features 。不同品种(PA6/PA66/PA12等)可满足从 general purpose 到高 heat resistant 各种需求。

📦 储存 and 处理建议

nylon 类 resin 均 has 较强 moisture absorption property ，必须储存 in 干燥密封环境 in 。 processing 前80°C干燥4小时以上(除湿干燥机推荐)。开封后尽快使用，含水率控制 in 0.1%以下。

🌍

RoHS 合规

符合欧盟RoHS指令

🏭

ISO 认证

质量管理体系

✅

quality assured

原厂正品

更多 engineering plastics Model 请访问daoqinsh.com

📐 详细物 property 参数表

测试项目	典 type 值	测试标准	单位
density	1.12-1.15	ASTM D792	g/cm³
melt flow index (MFR)	5-80	ASTM D1238	g/10min
melt temperature	215-225	ASTM D3418	°C
tensile strength (干态)	60-85	ASTM D638	MPa
tensile strength (调湿态)	45-60	ASTM D638	MPa
断裂伸长率(干态)	50-300	ASTM D638	%
flexural modulus (干态)	2500-3000	ASTM D790	MPa
flexural strength (干态)	85-120	ASTM D790	MPa
悬臂梁缺口 impact (干态)	50-150	ASTM D256	J/m
洛氏 hardness	R118-R122	ASTM D785	—
heat deflection temperature (HDT) (0.45MPa)	180-210	ASTM D648	°C
heat deflection temperature (HDT) (1.8MPa)	65-80	ASTM D648	°C
line property thermal expansion coefficient	60-80	ASTM D696	10⁻⁶/°C
体积电阻率	>10¹²	ASTM D257	Ω·cm
介电强 degree	15-25	ASTM D149	kV/mm
friction coefficient	0.15-0.35	ASTM D1894	—
water absorption (24h/饱 and)	1.8/3.0	ASTM D570	%
molding shrinkage	0.7-1.5	ASTM D955	%
UL94 flame retardant rating	V-2	UL 94	—

* 以上数据 is 典 type 参考值，具体以原厂TDS is 准

If you have any questions about Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer, or would like to request Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer datasheet, MSDS, ROHS test report, SGS report, REACH certificate, FDA certificate, EU regulation certificate, UL certificate, or COC/COA report, please call our service hotline +86-192-7986-4570, or click Contact Us to leave us a message.

Product Features

Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer Properties, Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer Product Parameters, Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer Performance Data, Clariant AddWorks TFB 117 polyamide (PA) nylon use light hot 协同 stabilizer Factory Report, MSDS, Material Safety Data Sheet, UL Yellow Card, SGS Report, RoHS, Food Grade Certification, NSF Drinking Water Standard, Product Information, Product Performance, Factory Report, Original Packaging, Authorized Distributor, Heat Deflection Temperature, Melt Index, Flow Coefficient, Impact Resistance, Impact Strength, Low Temperature Toughness, Low Temperature Impact Resistance, Melt Flow Rate, Processing Technology, Processing Parameters, Processing Temperature, EU RoHS, German FDA, US FDA, Japan FDA