Shanghai Daoqin Plastics Co., Ltd.

        PVC plastics products types type more, application non 常广泛. summary 20+ PVC products use formulation (use amount is quality 份), and large separation 享!

        PVC排 water tube/pipe

        1, PVC 100, heavy 钙 200, combined formed heavy 钙 50, composite/compounding salt stabilizer 5.6, hard acid 1.8, wax 0.3, CPE 10, titanium powder 3.6.

        2, PVC 100, 300目 heavy 钙 50, 80目 heavy 钙 150, hard acid 0.8, wax 0.55, composite/compounding salt stabilizer 4-5, CPE 4.

        3, PVC 100, heavy 钙 125, light 钙 125, stabilizer 6.2, wax 1.5, hard acid 1.3, titanium powder 4, CPE 10, PE wax 0.3, increase agent 0.03.

        4, PVC 100, heavy 钙 250, light 钙 50, hard acid 2.4, wax 2.6, CPE 6, salt stabilizer 5.0.

        5, PVC 100, hard acid 1.0, wax 0.8, salt stabilizer 4.6, heavy 钙200.

        6, PVC 100, light 钙 25, salt stabilizer 3.5, mono 甘脂 1.1, PE wax 0.3, hard acid 0.2, ACR(400) 1.5, wax 0.35, titanium powder 1.5, 群青 0.02, increase agent 0.02.

        PVC to water tube/pipe

        1, PVC 100, zinc composite/compounding stabilizer 3.5, light 钙 5, PE wax 0.15, hard acid 0.2, CPE 3-6, ACR(401) 1.0-2.0, titanium powder 2-4, increase agent amount. quality water tube/pipe can use salt composite/compounding stabilizer.

        2, PVC 100, composite/compounding salt stabilizer 2.4, wax 0.1, PE wax 0.13, hard acid 0.3, mono 甘脂0.3, CPE 4, ACR(400 or 90S) 1.0, light 钙 20, titanium powder 1.0.

        PVC pipe fittings

        1, PVC(SG-7) 100, heat stabilized agent 3.5, DOP 3.0, ACR(100 or 200)1.5, PE wax 0.6, inner lubricant (hard acid or high quality mono 甘脂) 1.2, light carbon acid 钙 25.

        2, PVC(SG-7) 100, heat stabilized agent 3.8, DOP 3.0, ACR(100 or 200)2.0, PE wax 0.35,石 wax 0.3, hard acid 0.3, mono 甘脂 1.2, light carbon acid 钙 35, 群青0.02, light increase agent 0.02.

        PVC穿线 tube/pipe

        1, PVC 100, light 钙 30, stabilizer 3.2, wax 0.6, hard acid 0.4, titanium powder 1, CPE 6.

        2, PVC 100, light 钙50, salt stabilizer 3.8, CPE 8, wax 0.3, hard acid 0.8, titanium powder 0.8.

        PVC线 box/case

        PVC 100, light 钙30, composite/compounding salt stabilizer 3.6, ACR 2.0, DOP 3, hard acid 1.0, wax 0.3, PE wax 0.35, increase agent 0.02, titanium powder 1.6.

         medical grade PVC plastics tube/pipe

        PVC 50, 均苯四 acid ester 35.52, ring oxygen large 豆油 1.89, hard acid 0.15, Ca/Za environmental protection stabilizer 1.0, alcohol 0.048, PE wax 0.1.

        PVC transparent tube/pipe

         soft tube/pipe: PVC 100, DOTP 45, ring oxygen large 豆油 5, hard acid 0.4, PE wax 0.35, has machine 锡1.5.

         hard tube/pipe: PVC100, has machine 锡1.4, MBS 5.0, ACR(40) 0.6, inner lubricated 60 0.6, 74/70S 0.5.

        PVC transparent sheet/slice 材

        PVC(SG-7/8) 100, has machine 锡 0.8-1.2, ACR(40)0.8, MBS 2-4, OK-60 0.8, 70S 0.5, light increase agent 0.002, 群青 0.001.

        PVC construction sheet/plate

        1, PVC(SG-8)50, light 钙 25, composite/compounding salt stabilizer 2.3, white foaming agent 0.45, foaming agent AC 0.3, powder 10, PVC recycling material 20, foaming adjustment agent (80) 4, CPE 2, hard acid 0.35, PE wax 0.25.

        2, PVC 75, light 钙35, material 50, foaming sheet/plate waste material 20, salt composite/compounding stabilizer 3.6, foaming adjustment agent (533) 9.5, PE wax 0.55, OA6 or 316A 0.5, AC foaming agent 0.3, white foaming agent NC 0.8.

        PVC扣 sheet/plate

        1, PVC 100, heavy 钙220, PE wax 1.2, hard acid 2.0, DOP 4.0, CPE 8.0, salt composite/compounding stabilizer 5.2, titanium powder 3.0, light increase agent 0.02.

        2, PVC 100, heavy 钙200, salt composite/compounding stabilizer 5.6, wax 1.2, hard acid 2.4, DOP 3.0, CPE 8.0, titanium powder 3.0, light increase agent 0.03.

        3, PVC 100, heavy 钙250, salt composite/compounding stabilizer 5.6, wax 1.4, hard acid 2.4, DOP 3.0, CPE 8.0, abrasion powder material 40.

        PVC sheet/plate

        1. calendering sheet/plate 革:PVC 100, heavy 钙60, salt composite/compounding stabilizer 2.5, PE wax 0.25, ACR(100) 1-2, hard acid 0.3, DOP 32, titanium powder 1.0, light increase agent 0.05, 群青 0.18.

        2. sheet/plate 布:PVC 50, dilute stabilizer 2.0, wax 0.6, hydrogen oxidation 镁 16, light carbon acid 钙 15, DOP35, chlorine wax 15, hard acid 0.6, color powder amount.

        3. sheet/plate 基材:PVC 75, light 钙85, zinc composite/compounding stabilizer 4.2, foaming adjustment agent (80) 8, AC foaming agent 0.25, white hot foaming agent 0.6, 316A 0.4,,60 0.70, PE wax 0.55, material 40;

         or PVC 75, light 钙 75, zinc composite/compounding stabilizer 4.0, foaming adjustment agent (80)7.2, AC foaming agent 0.25, white hot foaming agent 0.6, 316A 0.35,60 0.70, PE wax 0.5, material 30.

        PVC resin 瓦

        1, abrasion powder material 125, light 钙25, stabilizer 3.0, CPE 5, hard acid 0.5, PE wax 0.5.

        2, PVC 100, salt composite/compounding stabilizer 4.0, CPE 5, hard acid 1.4, wax 0.4, PE wax 0.5.

        PVC type 材

        1, PVC(SG-5) 100, composite/compounding 铅 4, hard acid 0.3, PE wax 0.25, ACR(400 or 90s)2, CPE(35%) 10, active property light 钙 15, titanium powder 2.5.

        2, PVC(SG-5) 100, zinc stabilizer 4.2, hard acid 0.3, wax 0.3, mono 甘脂0.3, ACR(801 or 90S)2, CPE(35%) 10, light 钙 40, titanium powder 4.5, 群青0.02, increase agent 0.012.

        PVC结皮 foaming sheet/plate

        1, PVC(700)100, salt composite/compounding stabilizer 4.4, light 钙 60, foaming adjustment agent (921) 10.5, AC 0.65, NC 1.5,316A 0.6, PE wax 0.4, 6A 0.2,60 0.8, titanium powder 2.0, increase agent 0.04, 群青 0.03, abrasion powder material 60.

        2, PVC 75, salt stabilizer 3.3, AC 0.4, foaming 1.1, inner slip 60 0.7, 316A 0.48, PE wax 0.35, 6A 0.2, foaming adjustment agent (920) 8.5, light 钙 55-60, material 40.

        PVC自由 foaming sheet/plate

        1, PVC(700)100, salt composite/compounding stabilizer 4.0, light 钙 40, foaming adjustment agent (418/80) 10, AC 0.5, 316A 0.54, PE wax 0.36, 6A 0.2,60 0.45, titanium powder 2.0, increase agent 0.04, 群青 0.03, abrasion powder material 40-50.

        2, PVC(700)100, salt composite/compounding stabilizer 4.0, light 钙 40, foaming adjustment agent (418/80) 8-10, AC 0.38, 316A 0.62, PE wax 0.3, 6A 0.3,60 0.6, titanium powder 4.0, increase agent 0.08, 群青 0.03, abrasion powder material 30-60.

        PVC密封 strip/profile

        1, PVC 100, has machine 锡 1.8, DBP 64, chlorine wax 28, hard acid 0.8, PE wax 0.6.

        2, PVC(SG-5)100, DOS 45, DBP 60, light 钙 150, hard acid 1.4, wax 0.8, salt stabilizer 3.2, material amount.

        3, PVC100, light 钙170, DOP 50, chlorine wax 25, hard acid 1.5, wax 0.75, salt stabilizer 3.25.

        PVC high filling 木塑

        PVC 100, salt composite/compounding stabilizer 5.6, foaming adjustment agent (100)11, mono 甘脂4.0, PE wax 1.2, hard acid 0.5, powder 30, powder 200, AC foaming agent 2.0, material amount, material 60.

        PVC木塑墙 sheet/plate

        1, PVC-8 25, small tube/pipe material 100, light 钙 50, powder 7, CPE 5, material 25, salt stabilizer 1.8, foaming adjustment agent (100/418/80)5,AC 0.35,白 foaming 0.6, PE wax 0.5, hard acid 0.6, material amount.

        2, PVC-8 50, light 钙 50, powder 5, CPE 3, material 30, salt stabilizer 3.0, foaming adjustment agent (100/418/80)6,AC 0.55,白 foaming 0.5, PE wax 0.5, hard acid 0.6, material amount.

        3, small tube/pipe material 75, light 钙 50, material 50, powder 8, PVC 12.5, stabilizer 2.0, foaming adjustment agent (100/418/80)6-8, AC 0.6, foaming 1.0, PE wax 0.3, hard acid 0.5, material amount.

        4, PVC-8 75, light 钙 80, powder 5, CPE 2, material 25, salt stabilizer 4.3, foaming adjustment agent (100/418/80)6-8,AC 0.6,白 foaming 0.9, PE wax 0.6, hard acid 0.8-1.2, material amount.

        PVC木塑门 strip/profile

        1, PVC 25, small tube/pipe material 108, heavy 钙 75, stabilizer 2.5, CPE 4, adjustment agent (90S)8.0, AC 0.8, PE wax 0.2, hard acid 0.2.

        2, PVC 25, light 钙 50, small tube/pipe material 50-75, material 25, powder 8, PE wax 0.3, hard acid 0.4, salt stabilizer 1.8, AC 0.65, foaming adjustment agent (90S)3.5.

        PVC foaming shoe sole

        1, PVC 100, DOP 80-85, light 钙 60-65, AC 0.5-0.6, foaming adjustment agent (90S)2.0 left right, salt composite/compounding stabilizer 3.8, PE wax 0.6, hard acid 1.0, color powder amount.

        2, PVC 100, DOP 90, light 钙 70, AC 0.8, foaming adjustment agent (90S)2.0 left right, salt composite/compounding stabilizer 4.0, PE wax 0.8, hard acid 1.2, color powder amount.

        3, PVC 100, DIBP 85, light 钙 60, AC 0.5, foaming adjustment agent (90S)2.0 left right, zinc composite/compounding stabilizer 4.0, PE wax 0.2, hard acid 0.3, color powder amount.

         flame retardant environmental protection cable material

        护层: PVC 100, TOTM 50, ring oxygen large 豆油5, chlorine wax 8, oxidation 二锑 5, resistant oxidation agent 0.5, 煅烧陶土 5.0, light 钙 10, zinc stabilizer 7, PE wax 0.2, hard acid 0.3.

         insulation: PVC100, TOTM 45, ring oxygen large 豆油3, chlorine wax 8, oxidation 二锑 4, resistant oxidation agent 0.4, 煅烧陶土 10, light 钙 15, zinc stabilizer 7, PE wax 0.25, hard acid 0.3.

        PVC hot shrink film

        PVC 50, hard acid 钙 0.3, hard acid 0.25, ACR(20/175)0.3-0.8, nano 钙 0.3, wax 0.25, DOP 2.5, large 豆油 2, zinc stabilizer 1.6(or has machine 锡 1.3), increase agent 0.005.

        PVC hot shrink sleeve/set tube/pipe

        PVC(SG-6/7)100, light 钙10, salt stabilizer 3.0, CPE 6-8, DOP 5, wax 0.3, hard acid 0.6, masterbatch amount.